KẾT QUẢ BƯỚC ĐẦU VỀ NGHIÊN CỨU ĐÁNH GIÁ ĂN MÒN CỌC BÊ TÔNG DỰ ỨNG LỰC TRONG MÔI TRƯỜNG BIỂN TẠI PHÒNG THÍ NGHIỆM

 Abstract - 03 concrete piles (200 mm x 200 mm x 1500 mm) were prepared by using type of concrete C70, C80, C90 and prestressting steel 7.10 mm. These piles were exposured to wet (03 days)/dry (04 days) test cycle in 04 months. The corrosion of prestressting steel in concrete piles was evaluated Using Half-cell Potential method and test content of chloride ion . Preliminary results shows that prestressing steels in concrete piles were not corroded; The results of corrosion potential were high than – 200 mV CSE and  the chloride ion ingress into concrete is small. The study is continuing to collect new data.

Từ khóa: Cọc bê tông dự ứng lực, cáp dự ứng lực, điện thế ăn mòn, điện cực so sánh Cu/CuSO₄, xâm nhập clo, ăn mòn.

Keywords: Prestressed concrete pile, prestressing steel, corrosion potential, Cu/CuSO₄ electrode, chloride ingress, corrosion.

Thông tin liên lạc của tác giả:

Họ và tên (tác giả số 1):         ThS. Nguyễn Thúy Hằng

Chức danh:                            Phó Giám đốc

Cơ quan:                                Viện CN VLXD&BVCT GTVT  - Viện KH&CN GTVT

Địa chỉ:                                   1252 Đường Láng – Đống Đa – Hà Nội

Điện thoại:                             098-808-0166

E-mail:                                    caotuanitst@gmail.com